Rilsan CLEAR G380是法国阿科玛ARKEMA原阿托菲纳(ATOFINA)生产的一种聚酰胺11聚合物材料。Arkema Rilsan PA11塑胶原料具有的高压爆 破强度,耐候性和抗紫外线性,低密度(比铝轻三倍,约为PA6密度的85%),很低吸湿性,特别耐低温,高耐冲击特性(优良的冷冲击强度),高抗拉强度,高断裂延伸率,的热性能,优良的抗裂纹扩展性和性,优良的耐化学腐蚀性(特别耐碳氢化合物、硫酸、氯化锌),易加工性(易挤出、注塑、吹塑、滚塑成型)。Arkema Rilsan® PA11部分牌号被批准用于食品接触或医疗行业。
Arkema Group Rilsan Clear G380(聚酰胺-尼龙11)
Physical Properties物理性质 | Metric公制数据 | English英制数据 | Comments测试 |
Density密度 | 1.01 g/cc | 0.0365 lb/in³ | ISO R 1183 D |
Water Absorption吸水率 | 1.3 % | 1.3 % | at e at 23°C and 50 % RH; ISO 62 |
3.3 % | 3.3 % | at e at 23°C in water; ISO 62 | |
Mechanical Properties力学性能 | Metric公制数据 | English英制数据 | Comments测试 |
Hardness, Shore D肖氏硬度D | 83 | 83 | instantaneous, conditioned 15 day, 23°C - 50 % R.H.; ISO 868 |
81@Time 15.0 sec | 81@Time 0.00417 hour | conditioned 15 day, 23°C - 50 % R.H.; ISO 868 | |
Tensile Strength at Break断裂拉伸强度 | 60.0 MPa | 8700 psi | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Tensile Strength, Yield屈服拉伸强度 | 55.0 MPa | 7980 psi | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Elongation at Break断裂伸长率 | >= 150 % | >= 150 % | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Elongation at Yield屈服伸长率 | 7.0 % | 7.0 % | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Tensile Modulus拉伸模量 | 1.69 GPa | 245 ksi | conditioned 15 days, 23°C - 50 % R.H.; ISO 527 |
Flexural Modulus弯曲弹性模量 | 1.53 GPa | 222 ksi | conditioned 15 days, 23°C - 50 % R.H.; ISO 178 |
Charpy Impact Unnotched夏比缺口试样冲击 | NB@Temperature 23.0 °C | NB@Temperature 73.4 °F | ISO 179/1eU |
NB@Temperature -30.0 °C | NB@Temperature -22.0 °F | ISO 179/1eU | |
Charpy Impact, Notched夏比缺口冲击 | 100 J/cm²@Temperature -30.0 °C | 476 ft-lb/in²@Temperature -22.0 °F | ISO 179/1eA |
110 J/cm²@Temperature 23.0 °C | 524 ft-lb/in²@Temperature 73.4 °F | ISO 179/1eA | |
Thermal Properties热性能 | Metric公制数据 | English英制数据 | Comments测试 |
Deflection Temperature at热变形温度 0.46 MPa (66 psi) | 110 °C | 230 °F | ISO 75 |
Deflection Temperature at热变形温度 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ISO 75 |
Glass TRansition Temp, Tg玻璃化温度 | 135 °C | 275 °F | ISO 11357 |
Shrinkage收缩, MD | 0.10 %@Thickness 2.00 mm | 0.10 %@Thickness 0.0787 in | after 24h, mould at 40°C |
Shrinkage收缩, TD | 0.50 %@Thickness 2.00 mm | 0.50 %@Thickness 0.0787 in | after 24h, mould at 40°C |
Optical Properties光学性质 | Metric公制数据 | English英制数据 | Comments测试 |
TRansmission, Visible透光率 | 90.0 % | 90.0 % | clear; thickness not quantified |
Processing Properties加工性能 | Metric公制数据 | English英制数据 | Comments测试 |
Processing Temperature加工温度 | 240 - 300 °C | 464 - 572 °F | Injection |
270 °C | 518 °F | Injection, recommended | |
Mold Temperature模具温度 | 20.0 - 80.0 °C | 68.0 - 176 °F | |
Drying Temperature干燥温度 | 70.0 - 80.0 °C | 158 - 176 °F | |
Dry Time干燥时间 | 4.00 - 6.00 hour | 4.00 - 6.00 hour | |
Component Elements Properties组件元素属性 | Metric公制数据 | English英制数据 | Comments测试 |
Carbon碳, C | 53 - 55 % | 53 - 55 % | renewable; ASTM 6866 |
- 现货 Arkema阿科玛PA11 Rilsan® CLEAR G350主要用途 2024-04-29
- 现货 Arkema阿科玛(阿托菲拉)PA11 CLEAR G170透明级尼龙11 2024-04-29
- 现货PA11 法国阿科玛 BMNO P20 TLD 耐候 抗紫外线 2024-04-29
- 现货 尼龙塑胶原料 PA11 法国阿科玛 BESN G9 TL 注塑挤出级 2024-04-29
- 现货 耐油 耐低温PA11 法国阿科玛 7492 涂覆级 油管 2024-04-29
- 现货 抗腐蚀 PA11 法国阿科玛3000 RNEW-1 耐紫外线 电线电缆应用 2024-04-29
- 现货 PA11 BZM80TL 法国阿科玛 热塑性 2024-04-29
- 现货 PA11 法国阿科玛 BESNO-TL 阻燃性 透明级 抗紫外线 2024-04-29
- 现货 耐老化PA11 法国阿科玛 BESN P40 NOIR T6L 油管原料 2024-04-29
- 现货 PA11 法国阿科玛 热塑性 BESN P40 BLK TL 耐化学性 2024-04-29
- 现货 法国阿科玛PA11 BESN P40 BLK T6L(液压管原材料) 2024-04-29
- 现货 PA11 法国阿科玛 BESNBLKP212CTL 热稳定性/耐水解 2024-04-29
- 现货 Arkema阿科玛PA11 Rilsan® POWDER D40 工程塑料 2024-04-29
- 现货 Arkema阿科玛PA11 Rilsan® POWDER ESY BLACK X 7260 塑胶原料 2024-04-29
- 现货Fine Powders T NAT BHV COS PA11 法国阿科玛 Rilsan 2024-04-29
联系方式
- 地址:东莞常平麦元村物流大道西段美吉特一期5栋20号
- 电话:0769-87187279
- 经理:马益群
- 手机:13711820929
- 传真:0769-87187279
- 微信:13711820929
- QQ:384974711
- Email:mayiqun10@126.com